Simple Approach For Preparing Post-Treatment-Free Solution Processed Non-Stoichiometric Niox Nanoparticles As Conductive Hole Transport Materials

ABSTRACT

High-quality non-stoichiometric NiO x  nanoparticles are synthesized by a facile chemical precipitation method. The NiO x  film can function as an effective p-type semiconductor or hole transport layer (HTL) without any post-treatments, while offering wide temperature applicability from room-temperature to 150° C. For demonstrating the potential applications, high efficiency is achieved in organic solar cells using NiO x  HTL. Better performance in NiO x  based organic light emitting diodes is obtained as compared to devices using PEDOT:PSS. The solution-processed NiO x  semiconductors at room temperature can favor a wide-range of applications of large-area and flexible optoelectronics.

FIELD OF THE INVENTION

The present invention relates to an improved method for providing hole transport layers for optoelectronic devices.

BACKGROUND OF THE INVENTION

Organic solar cells (OSCs) and organic light emitting diodes (OLEDs) have gained increasing attention owing to their superior advantages of low cost, light weight, and flexibility of a variety of optoelectronic applications. One of the critical aspects in fabricating highly efficient and stable optoelectronic devices is the design of the functional carrier transport layers between the organic active layer and the electrodes. Typically, effective hole transport layers (HTLs) in optoelectronic devices have to satisfy electrical and optical requirements of (1) high electrical conductivity, (2) good optical transparency with wide bandgap, (3) good electron blocking with efficient hole transport. Poly(3,4-ethylenedioxythiophene):poly(styrene-sulfonate) (PEDOT: PSS) with a work function (WF) of 5.10 eV has been widely used as HTL in optoelectronic devices, such as conventional organic optoelectronics. However, there are some issues of its electrical and physical inhomogeneity, such as the long-standing acidic nature of PSS regarding the poor stability and severe degradation of organic optoelectronic devices. Alternatively, stable transition metal oxides (TMOs) such as MoO₃, WO₃, V₂O₅ and NiO_(x), stand out as promising candidates for efficient HTLs. It is essential to develop a wide range of efficient and low-cost TMOs to serve as functional HTLs. Until now, low-temperature solution-processed approaches have been demonstrated for MoO₃, WO₃, and V₂O₅.

Differently, the valence band of NiO_(x) is well aligned with the highest occupied molecular orbital (HOMO) levels or valence band of many typical organic and inorganic semiconductors, respectively, for hole transport which is distinct from other typical oxide based HTL materials such as MoO₃, WO₃ and V₂O₅. Besides, NiO_(x) offers promising characteristics as an anode interlayer with wide bandgap semiconductor properties, good electron blocking and optical transparency. However, the fabrication of highly efficient NiO_(x) HTLs by a low temperature solution process still remains a great challenge. NiO_(x) is a cubic rock-salt structure with octahedral Ni²⁺ and O²⁻ sites. Pure stoichiometric nickel oxide is an excellent insulator with conductivity of 10⁻¹³ S cm⁻¹, while non-stoichiometric NiO_(x) is a wide bandgap p-type semiconductor. Due to the positive charge compensation induced by thermodynamically favored cation vacancies, the non-stoichiometric NiOx shows a p-type conduction property.

The conventional ways of fabricating NiO_(x) usually involve thermal annealing processes and oxygen-plasma treatment, which hinders the applications of NiO_(x) in flexible optoelectronic devices (i.e. OLED/OSC).

BRIEF SUMMARY OF THE INVENTION

The present invention is directed to a chemical precipitation method for synthesizing NiO_(x) nanoparticles. The synthesized NiO_(x) can be used for producing NiO_(x) HTL film in a room temperature solution process without any post-treatments during device fabrication.

Embodiments of the subject invention are drawn to a new approach, i.e., a chemical precipitation and combustion method creating HTLs is achieved by forming non-stoichiometric NiO_(x) nanoparticles (NPs). The combustion in air promotes oxygen interactions with a nickel-deficient lattice, further forming different valence-state compositions, including NiO (Ni²⁺), NiOOH (Ni³⁺), and Ni₂O₃ (Ni³⁺). The resultant nanoparticles are non-stoichiometric NiO_(x) nanoparticles, which are important due to their dispersion in water, reaching up to a high concentration of 50 mg L⁻¹. The dark-black NiO_(x) nanoparticles (powders) are very stable after 6 months during storage in an ambient environment, and the NiO_(x) nanoparticle dispersions are stable after 15 days, and are still well dispersed without any precipitation or aggregation.

In an embodiment, a new approach can be used to form a NiO_(x) HTL film through a room temperature solution process without any post-treatments including oxygen-plasma treatment and annealing treatment. The results show that the NiO_(x) NPs film can function as effective HTLs over a wide range of annealing temperatures from room temperature to 150° C. The NiO_(x) NPs film has superior optical, electrical and surface properties, and the work function is well aligned with HOMO levels and the valence band of many typical p-type conjugated 4polymers and inorganic semiconductors.

In another embodiment of the invention organic optoelectronic devices, using the NiO_(x) NPs film as HTLs and commercially available polymer/organic materials as the active layer of organic solar cells (OSC), high power conversion efficiency (PCE) of 9.16% with V_(OC) of 0.794 V, J_(SC) of 18.32 mA cm⁻² and FF of 63.10% is achieved, which causes a noticeable enhancement compared with the control device using PEDOT:PSS as HTLs (PCE of 8.60%, V_(OC) of 0.782 V, J_(SC) of 18.03 mA cm ⁻² and FF of 60.97%). The NiO_(x) NPs film can also function as HTLs in organic light emitting diodes (OLEDs) based on the use of commercially available polymer/organic materials as the active layer. The OLED devices have a turn-on voltage of 3.75 V, a maximum brightness of 26630 cd m⁻² at 11.25 V, a current efficiency is 9.72 cd A⁻¹, which is higher than that of PEDOT:PSS-based devices with a maximum brightness of 23100 cd m⁻² at 12.50 V and a current efficiency of 9.20 cd A⁻¹. The results reveal that both OLEDs and OSCs with efficient NiO_(x) HTLs can be comparable and competitive with that of PEDOT:PSS.

In a further embodiment, the synthesize method is a low cost process: no expensive and hi-tech equipment is required (only OSC and OLED devices fabrication is need), low cost materials (commercially available materials of Ni(NO₃)₂·6H₂O and NaOH), low energy consumption (low reaction time is only about five minutes, combustion process only needs 2 hours of energy consumption). In ambient environment, the NiO_(x) based OSC devices show much better stability compared to the devices using PEDOT:PSS as HTLs.

The room temperature process for the formation of conductive thin films according to the invention can be applicable to various substrates, including flexible substrates which will deform upon thermal annealing and are not compatible with high temperature processes.

BRIEF DESCRIPTION OF THE DRAWINGS

The foregoing and other objects and advantages of the present invention will become more apparent when considered in connection with the following detailed description and appended drawings in which like designations denote like elements in the various views, and wherein:

FIG. 1(a) is a TEM image of non-stoichiometric NiO_(x) NPs with scale bar of 20 nm and FIG. 1(b) is a X-ray diffractometry line broadening (XRD-LB) result of NiO_(x);

FIG. 2(a) is a XPS result of NiO_(x) films of Ni 2p_(3/2) core level peaks and FIG. 2(b) is a XPS result of NiO_(x) films of O 1 s core level peaks;

FIGS. 3(a), 3(b) and 3(c) is energy-level diagrams of the investigated NiO_(x) films (20 nm) with no annealing, 100° C. annealing and 200° C. annealing, respectively;

FIGS. 4(a) to 4(c) are current density-voltage (J-V) characteristics for PCDTBT, PTB7 and PTB7-Th, respectively, and FIG. 4(d) is an IPCE curve for the same materials; and

FIG. 5(a) is a J-V-L curve and FIG. 5(b) is a LE-J-L curve of OLEDs, PEDOT:PSS and NiO_(x).

DETAILED DISCLOSURE OF THE INVENTION

The subject invention relates to a new facile chemical precipitation and combustion method which is robust and simple for direct preparation of high quality non-stoichiometric NiO_(x) NPs. By using this method, NiO_(x) HTL film can be formed through a room temperature solution process without any post-treatments during device fabrication. Such a NiO_(x) HTL film can be used in many applications, including but not limited to flexible optoelectronics, organic solar cells, organic light emitting diodes, and organic photodetectors.

NiO_(x) NPs can be obtained by a chemical precipitation and combustion method using commercially available materials of Ni(NO₃)₂·6H₂O and NaOH. The raw materials are easily dissolved in deionized water. After dropwise adding NaOH, the clear green aqueous solution turns turbid. By accurately controlling the solution pH value to 10, a considerable yield of ultrafine nickel hydroxide Ni(OH)₂ is obtained. The obtained apple-green product is dried and calcined at 270° C. for two hours in air to decompose into dark-black NiO_(x) NPs. This calcination procedure is based on the thermal decomposition of Ni(OH)₂ aiming to produce non-stoichiometric NiO_(x) NPs. The dark-black NiO_(x) nanoparticles (powders) are very stable after 6 months during storage in an ambient environment, and the NiO_(x) nanoparticle dispersions are stable after 15 days, and are still well dispersed without any precipitation or aggregation.

Equations 1 and 2 illustrate the chemical reactions in this procedure of forming non-stoichiometric NiO_(x) NPs:

X-ray diffraction (XRD) to investigate the NiO_(x) crystal structure and dimensions reveals diffraction peaks which show the NiO_(x) as a cubic crystal structure. Three prominent characteristic diffraction peaks of NiO_(x) cubic structure appear at 2θ which equals 37.11°, 43.08° and 62.25°, respectively. Among them, the strongest diffraction peak is observed when 2θ is 43.08°, which demonstrates that the NiO_(x) NPs have already crystallized. The diameter (D) of the NiO_(x) NPs is calculated by Debye-Scherrer equation: D=0.89λ/(β cos θ), from which it can be determine that the average crystalline size is 4 nm. Meanwhile, as shown in the transmission electron microscopy (TEM) results of FIG. 1, the NiO_(x) nanoparticles with a good uniformity can be obtained. The particle size is about 3-5 nm, which is consistent with the X-ray diffractometry line broadening (XRD-LB) results.

The optical, electrical and surface properties of the NiO_(x) thin films were examined by using different techniques. The NiO_(x) dispersion was prepared by dispersing the NiO_(x) NPs into water to a desired concentration from 5 mg ml⁻¹ to 50 mg ml⁻¹. The NiO_(x) dispersion was spin-coated on pre-cleaned indium tin oxide (ITO) glass. The resultant NiO_(x) films were annealed at different temperatures (from no annealing to 300° C.) under ambient environment. The thicknesses of corresponding NiO_(x) films were ca. 4 nm (5 mg ml⁻¹), 12 nm (15 mg ml⁻¹), 20 nm (30 mg ml⁻¹) and 32 nm (50 mg ml⁻¹), which were measured by ellipsometry.

To demonstrate the capability of NiOx films to perform as highly efficient HTL over a wide range of temperatures, X-ray photoelectron spectroscopy (XPS) analysis was used to investigate the chemical composition of the NiO_(x) films processed under different temperatures. The Ni 2p 3/2 and O 1 s characteristic peaks of the NiO_(x) film in XPS spectra are shown in FIG. 2. The decomposition of the XPS spectrum demonstrates that the Ni 2p spectrum can be well fitted by two different oxidation states (Ni²⁺ and Ni³⁺) in the form of a Gaussian function. When the NiO_(x) film receives no annealing treatment or other UVO or O₂-plasma treatment, rather remarkable contributor peaks of Ni³⁺ state such as NiOOH (Ni 2p 3/2 at 856.3 eV and O 1 s at 532.1 eV), Ni₂O₃ (Ni 2p 3/2 at 855.0 eV and O 1 s 530.8 eV), and another Ni²⁺ state NiO (Ni 2p 3/2 at 853.6 eV and O 1 s 529.1 eV) appear. As calculated from the integral area in the Ni 2p spectrum, the three composition concentration ratio of NiOOH, Ni₂O₃, and NiO is about 1.13:1.22:1 and the atomic ratio between Ni and O is about 1:1.14, which illustrates that the composition of the nickel oxide is non-stoichiometric. The result is completely different from the previously reported ones that only additional simultaneous O₂-plasma or UVO treatment or annealing treatment can lead to the formation of Ni³⁺ state in NiOOH species. Meanwhile, after 100° C. annealing treatment of the NiO_(x) film, no apparent shift or change of the dominant peaks in the Ni 2p 3/2 and O 1 s spectra was observed, which indicates that the major composition of the NiO_(x) thin films remains unchanged. However, when the annealing temperature is above 200° C., the composition of NiO_(x) film changes such that NiOOH peaks are weakened and the Ni₂O₃ peaks are strengthened in the XPS spectra in FIGS. 2a and b . The variation in characteristic peaks by 200° C. annealing suggests a partial composition conversion from NiOOH to Ni₂O₃. Upon high temperature annealing, the change in the non-stoichiometric NiO_(x) film composition where excessive Ni₂O₃ is generated, can have a detrimental impact on the electrical properties and thus the device performance of the NiO_(x) HTL. As a result, in addition to room temperature, the NiO_(x) NPs are able to form effective and stable HTL over a wide range of annealing temperatures up to 150° C. without inducing detrimental changes in composition.

Ultraviolet photoelectron spectroscopy (UPS) was utilized to investigate the energy band structures of the as-deposited and annealed NiO_(x) films at different temperatures. As calculated from the UPS results, the band diagram parameters including vacuum level (E_(Vac)), conduction band (CB), E_(F) and valence band (VB) are shown in FIG. 3. The as-deposited NiO_(x) films show an E_(F) of 5.25 eV. The appropriate E_(F) of post-treatment-free NiO_(x) film favors ohmic contact formation to HOMO of donor materials in bulk heterojunction (BHJ). The CB of NiO_(x), which is 1.85 eV from vacuum level, allows NiO_(x) to serve as an effective electron blocking layer to suppress electron recombination at the anode. The VB is 0.24 eV below the E_(F), indicating that NiO_(x) is a typical p-type semiconductor. After 150° C. annealing treatment, the E_(F) of the film is slightly changed to 5.13 eV, accompanied with CB of 1.76 eV and VB of 5.40 eV, which was almost the same with the as-deposited NiO_(x) film. However, when the NiO_(x) film is annealed at 200° C., the E_(F) of the NiO_(x) significantly decreases from 5.25 eV to 4.61 eV. Both the CB and VB decrease to 1.33 eV and 4.97 eV respectively, which indicates that the electrical properties of the film have been modified. Due to the larger energy mismatch with the HOMO of the donor materials (usually above 5.0 eV), the NiO_(x) film annealed at 200° C. can no longer function as an effective HTL. These results are consistent with the XPS results described previously, where the NiO_(x) and oxidation states of the metal oxide are changed at relatively high temperature (over 200° C.).

To demonstrate that the NiOx film can function as an effective HTL, OSCs were fabricated and characterized. Four polymers with different bandgaps, P3HT, PCDTBT, PTB7 and PTB7-Th with HOMO energy levels of 5.00 eV, 5.30 eV, 5.14 eV and 5.22 eV respectively, were used to examine the effect of NiO_(x) film as an efficient HTL. Device optimization was mainly focused on fine adjustment of the thickness and annealing temperature of the NiO_(x) film. OSCs with conventional structure of ITO/NiO_(x)/Active layer/Ca (20 nm)/Al (100 nm) were fabricated. OSCs with PEDOT:PSS (34 nm) HTLs were also compared as a control. The current density-voltage (J-V) characteristics of P3HT devices using NiO_(x) with different annealing temperatures were plotted in Table 1. It can be clearly seen that all the devices show similar performances from w/o annealing to 150° C. The results confirm that the film has mostly the same composition and WF below 150° C. annealing temperature, which is consistent with the XPS and UPS analytic results. Meanwhile, an annealing temperature over 200° C. significantly degrades the device performance due to a mismatch of WF of the NiO_(x) to the HOMO of P3HT. The results demonstrate that the NiO_(x) films in this work can function as effective HTLs without any post-treatment, as well as offer a wide temperature applicability from room-temperature to 150° C.

The optimized NiO_(x) films were then applied to low bandgap polymers such as PCDTBT (E_(gap)=1.70), with a larger V_(OC) due to the ionization potential (IP) higher than P3HT, to demonstrate its applicability to work as efficient HTL for low bandgap polymers. The WF of NiO_(x) (5.25 eV) is very close to the HOMO level of the donor polymer PCDTBT (5.30 eV), which can enhance the hole extraction from the photoactive layer. A comparison of the illuminated current density-voltage (J-V) measurements for both NiO_(x) and PEDOT:PSS based devices is presented in Table 2. The PCDTBT:PC₇₁BM devices employing PEDOT:PSS HTL exhibited an average V_(OC) of 0.878 V, J_(SC) of 10.81 mA cm⁻² and FF of 57.52% to yield a PCE of 5.45%. While utilizing the NiO_(x) thin film as HTLs, a remarkable 17.8% increment in device performance accompanied by an average V_(OC) of 0.906 V, J_(SC) of 11.36 mA cm⁻², FF of 62.35% and PCE of 6.42% was realized. The significant enhancement was mainly due to the ability of NiO_(x) to form favorable energetic alignment with the active layer, as compared to the alignment formed with PEDOT:PSS. This result is comparable to some reported device performance in the literature for NiO_(x) films prepared by other techniques. In addition, different from PEDOT:PSS, the E_(opt) of the NiO_(x) is 3.64 eV, indicating that the conduction band is 1.85 eV above the LUMO of the donor PCDTBT (3.60 eV) and acceptor PC₇₁BM (4.00 eV). This energetic orientation provides 1.75 eV to 2.15 eV energy barriers to electron collection at the anode and thus demonstrating effective electron-blocking properties of the NiO_(x) which contributes to an increment in V_(OC) through reducing leakage current and photocurrent recombination at the anode. The series resistance for the devices with NiO_(x) HTLs and the PEDOT:PSS reference devices was calculated to be 2.65 Ω cm² and 4.46 Ω cm², respectively. Improved contacts between active layer and anode, which facilitates free carriers extraction and transport, enhanced both J_(SC) and FF in the devices with NiO_(x) HTLs.

To demonstrate the general viability of NiO_(x) as an efficient HTL for low bandgap polymers, two PTB-derivatives, PTB7 (Egap=1.63 eV) and PTB7-Th (Egap=1.58 eV) were also selected to fabricate standard OSCs devices. FIG. 4a shows the J-V curves PCDTBT. FIGS. 4b and 4c show the J-V curves of the PTB7 and PTB7-Th based BHJ OSCs with the PEDOT:PSS or NiO_(x) HTLs, respectively. For PTB7:PC₇₁BM based devices, device performance with NiO_(x) HTL has a V_(OC) of 0.744 V, J_(SC) of 16.10 mA cm⁻², FF of 66.42%, and PCE of 7.96%, which is slightly higher than PEDOT:PSS devices (V_(OC) of 0.735 V, J_(SC) of 15.84 mA cm ⁻², FF of 63.63% and PCE of 7.41%). The results show the same energy alignment ability with a low band gap polymer PTB7 based device. The NiO_(x) HTL calculated J_(SC) (16.05 mA cm⁻²) from the IPCE spectra matched well with the J_(SC) (16.10 mA cm ⁻²) recorded from the J-V curves. The maximum IPCE spectrum in NiO_(x) devices is over 70%, indicative of highly efficient photon-to-electron conversion. For PTB7-Th:PC₇₁BM based OSCs, the device with NiO_(x) HTL has an average PCE of 9.16% with V_(OC) of 0.794 V, J_(SC) of 18.32 mA cm⁻² and FF of 63.10%, which has a noticeable enhancement compared with the PCE of the control device using PEDOT:PSS (PCE of 8.60% with a V_(OC) of 0.782 V, J_(SC) of 18.03 mA cm⁻² and FF of 60.97%). The R_(S) with NiO_(x) HTLs and PEDOT:PSS devices were 2.20 Ω cm² and 3.37 Ω cm², respectively. Rationalized by a similar rule as noted above, the reduced R_(S) results in better electrical contact thus improved FF, which is beneficial for device performance. The OSCs with the 20 nm NiO_(x) HTL shows higher IPCE at wavelengths of 500-700 nm compared with PEDOT:PSS HTL as shown in FIG. 4d . The IPCE maximum is over 80%, indicating an effective charge carrier generation and collection property. The calculated J_(SC) 18.28 mA cm⁻² from the IPCE spectra is consistent with the J_(SC) 18.32 mA cm⁻² recorded from the J-V measurements. Consequently, the efficient hole transport property of our low-temperature processing NiO_(x) HTLs comparable to PEDOT:PSS is demonstrated with different bandgap polymeric donors in OSCs.

OLEDs employing solution-processed NiO_(x) as HTLs were fabricated with a conventional structure of ITO/NiO_(x)/emission layer (80 nm)/Ca (20 nm)/Al (100 nm) where the emission layer is poly[2-(4-(3′,7′-dimethyloctyloxy)-phenyl)-p-phenylene-vinylene] (P-PPV). OLEDs with PEDOT:PSS (34 nm) HTLs were also compared as a control. The current density-voltage-luminance density (J-V-L) characteristics and luminance efficiency-current density-luminance (LE-J-L) characteristics for devices are shown in FIGS. 5a and 5b , respectively. The NiO_(x) film based devices had a turn-on voltage of 3.75 V, a maximum brightness of 26630 cd m⁻² at 11.25 V, a current efficiency of 9.72 cd A⁻¹, which is slightly higher than that of PEDOT:PSS-based devices with a maximum brightness of 23100 cd m⁻² at 12.50 V, and a current efficiency of 9.20 cd A⁻¹. The results reveal that OLEDs with efficient NiO_(x) HTLs can be comparable and competitive with that of PEDOT:PSS HTLs.

Following are examples that illustrate the procedures for practicing the invention. These examples should not be construed as limiting.

EXAMPLE 1

The OSCs based on P3HT were fabricated by using the conventional structure of ITO/NiO_(x)/Active layer/Ca (20 nm)/Al (100 nm). With different annealing temperature of NiO_(x) film, the device performances of OSCs based on P3HT are summarized in Table 1.

TABLE 1 Device performance at different annealing temperatures for NiO_(x) based OSCs with conventional structure of ITO/NiO_(x)/P3HT:PC₆₁BM/Ca/Al. NiO_(x) Annealing V_(OC) J_(SC) FF R_(S) PCE Temperature (V) (mA cm⁻²) (%) (Ω cm²) (%) w/o 0.588 ± 0.001 9.72 ± 0.24 67.31 ± 0.76 2.10 ± 0.07 3.83 ± 0.10  50° C. 0.587 ± 0.003 9.68 ± 0.31 66.16 ± 0.80 2.24 ± 0.10 3.77 ± 0.15 100° C. 0.588 ± 0.002 9.67 ± 0.16 67.20 ± 0.62 2.13 ± 0.04 3.81 ± 0.07 150° C. 0.581 ± 0.004 9.82 ± 0.22 66.50 ± 0.65 2.16 ± 0.07 3.80 ± 0.09 200° C. 0.560 ± 0.004 9.01 ± 0.37 57.90 ± 1.35 4.17 ± 0.11 2.92 ± 0.24 300° C. 0.481 ± 0.008 8.96 ± 0.35 42.99 ± 2.58 7.36 ± 0.09 1.85 ± 0.32

EXAMPLE 2

The OSCs based on different bandgap polymers were fabricated by using the conventional structure of ITO/NiO_(x)/Active layer/Ca (20 nm)/Al (100 nm). The control OSCs were also fabricated by using PEDOT:PSS layer as comparisons. The device performance of OSCs based on different bandgap polymers with PC₇₁BM were summarized in Table 2.

TABLE 2 Device performances of PEDOT:PSS or NiO_(x) based OSCs using different bandgap polymers with PC₇₁BM. V_(OC) J_(SC) FF R_(S) PCE Device structures (V) (mA cm⁻²) (%) (Ω cm²) (%) PEDOT:PSS/PCDTBT 0.878 ± 0.003 10.81 ± 0.22 57.52 ± 0.79 4.46 ± 0.10 5.45 ± 0.18 NiO_(x)/PCDTBT 0.906 ± 0.002 11.36 ± 0.31 62.35 ± 0.72 2.65 ± 0.06 6.42 ± 0.20 PEDOT:PSS/PTB7 0.735 ± 0.003 15.84 ± 0.30 63.63 ± 1.05 2.62 ± 0.09 7.41 ± 0.16 NiO_(x)/PTB7 0.744 ± 0.004 16.10 ± 0.27 66.42 ± 0.66 1.74 ± 0.05 7.96 ± 0.20 PEDOT:PSS/PTB7-Th 0.782 ± 0.003 18.03 ± 0.21 60.97 ± 0.60 3.37 ± 0.08 8.60 ± 0.16 NiO_(x)/PTB7-Th 0.794 ± 0.002 18.32 ± 0.17 63.10 ± 0.45 2.20 ± 0.10 9.16 ± 0.12

Based on these results it can be seen that the NiO_(x) nanoparticles are highly efficient hole transport layers in optoelectronic applications based on several donor polymers with different HOMO energy levels. Compared with conventional PEDOT:PSS-buffered devices, the NiO_(x)-buffered OSCs and OLEDs achieve improved or comparable device performances. The excellent optoelectronic performances can be realized at room temperature without any post-treatments to form the HTL films. Due to the desirable work function, NiO_(x) is a useful as an efficient HTL for high IP donor materials in order to maximize device performance. The NiO_(x) HTLs can be applied to various optoelectronic devices, including not only OSCs, but also OLEDs.

It should be understood that the examples and embodiments described herein are for illustrative purposes only and that various modifications or changes in light thereof will be suggested to persons skilled in the art and are to be included within the spirit and purview of this application and the scope of the appended claims. In addition, any elements or limitations of any invention or embodiment thereof disclosed herein can be combined with any and/or all other elements or limitations (individually or in any combination) or any other invention or embodiment thereof disclosed herein, and all such combinations are contemplated with the scope of the invention without limitation thereto. 

What is claimed is:
 1. A method for preparing non-stoichiometric NiO_(x) nanoparticles, with a composition of NiO (Ni²⁺), NiOOH (Ni³⁺), and Ni₂O₃ (Ni³⁺), wherein the method comprises: using a base to react with Ni ions in water to form an electrically insulated and undispersed intermediate; grinding the intermediate to form it into a uniform grain size; combusting the intermediate in air to cause oxygen to interact with a nickel-deficient lattice and further form non-stoichiometric NiO_(x) nanoparticles.
 2. The method of claim 1, wherein the NiO_(x) nanoparticles have dark-black color or atrous color.
 3. The method of claim 1, wherein the NiO_(x) nanoparticles comprise vacancy-induced Ni²⁺ and Ni³⁺ composition.
 4. The method of claim 1, wherein the non-stoichiometric NiO_(x) nanoparticles contain nickel oxyhydroxide (NiOOH) which have a plurality of hydroxyl groups.
 5. The method of claim 1, wherein the step of using a base to form undispersed intermediate involves use of a dispersing agent that is water/methanol, water/ethanol, or water/other alcoholic solvents.
 6. A non-stoichiometric NiO_(x)nanoparticle film, wherein the non-stoichiometric NiO_(x) nanoparticle film is produced by using the non-stoichiometric NiO_(x) nanoparticles according to claim
 1. 7. The non-stoichiometric NiO_(x) nanoparticle film of claim 6, wherein the NiO_(x) nanoparticles film is formed through a room temperature solution process without any post-treatments.
 8. The method of claim 7, wherein said the NiO_(x) nanoparticle film has a work function of 5.25 eV, and possesses typical p-type semiconductor properties.
 9. A method of claim 8, wherein the NiO_(x) nanoparticle film is transparent and is placed on anITO/glass substrate and has an optical transparency of at least 85% when the film has a thickness of 30nm. 